White or Tan 0.7mm 610GSM or 18oz Silica Cloth Roll Silica Fabric Roll Silica Fire Blanket Roll Silica Welding Blanket Roll

• Customization: Available
• Certification: ISO
• Application: Wall/Roof Covering Cloth, Filter Cloth, Fiberglass Mesh Cloth, Blind, Removable Insulation Blanket Pad Cover Jacket
• Model NO.: HS600
• Surface Treatment: Vermiculite, Silicone etc.
• Weave Type: Satin
• Fiberglass Type: Silica
• Alkali Content: Alkali Free
• Nominal Thickness: 0.7mm
• Nominal Weight: 612g or 18oz
• Filament Diameter: 9um
• Width: 100cm
• Service Temperature: 1000ºC
• Color: White or Brown
• Sample: Available
• Properties: Fire Resistant, High-Temp Resistance
• Properties2: High Strength, Excellent Thermal Properties
• Properties3: Abrasion Resistant, High Dimensional Stability
• Properties4: Low Smoke Emission, Chemical Resistant
• Applications: Oven and Door Seals, Gaskets, Furnace Seals
• Applications2: Engine Exhaust Covers, Electrical Insulation
• Sio2 Content: ≥96%
• Soft Point: 1700ºC
• Transport Package: Bag+Carton+Pallet
• Specification: custom
• Origin: Jiangsu, China
• HS Code: 7019590000

Product Description

Leached silica fabric is manufactured from fiberglass fabric then leached (a process that removes impurities from the fabric) to provide a minimum 96% Silica content product. The standard leached silica fabrics are a cost-effective option.  This fabric is not preshrunk.

The product has excellent heat resistance properties and can be used for a long time in the environment of 1000 °C. The instantaneous heat resistance temperature can reach 1400 °C, the workbench remains in perfect condition for 15 seconds at 1600ºC and the softening point temperature is 1700 °C.

Compared with ceramic fiber cloth, it has smaller ablation rate and thermal shrinkage rate (close to 1%), no stimulation to human body, beautiful appearance and good hand feeling.

High silica cloths/fabrics are widely used in aerospace, metallurgy, chemical industry, building materials, fire protection and other industrial fields.

Properties:

• High Tensile Strength
• High heat resistance
• High Dimensional Stability,
• Low thermal shrinkage
• Fire resistance
• Good thermal conductivity
• Good chemical resistance
• Outstanding electrical properties
• Durability
• Insulation
• Non-asbestos products, Environment friendly
• Sound insulation
• Good filtration performance
• Good machinability

Applications:

• Electrical insulating material
• High temperature resistance, heat insulation, heat preservation, sealing material
• Welding heat insulation protection material
• Fireproof materials (making fireproof clothing, fireproof curtains, fire extinguishing felt, etc.)
• High temperature gas dust collection, liquid filtration
• Metal melt filtration and purification
• Car, motorcycle noise reduction, heat insulation, exhaust gas filtration
• High temperature and ablation resistance material
• Sound and heat protection
• Basic cloth for coatings and laminations
• Welding Blanket And Fire Blanket
• Expansion Joints
• Heat Shields and Containment
• Oven Door Seals
• Gasketing
• Used as the bindings of boiler for electrical machinery and appliances

Specifications

Style	Width(cm)	Norminal Weight		Norminal Thickness	Structure	SiO2 Content %	Yarn Count	Breaking Strength		Linear Shrinkage(%)	L.O.I(%)
		gsm	osy	mm				wrap	fill
HS300	92	300	9	0.3	Twill 3*1	≥96	18.5*12.5	≥400	≥300	6.8	8.4
HS600	92/100/127	610	18	0.7	Satin 8HS	≥96	18*13	≥800	≥500	7.8	8.4
HS880	100	880	26	1	Satin 12HS	≥96	18*13	≥1000	≥750	7.7	8.9
HS1100	92/100	1100	32	1.25	Satin 12HS	≥96	18*13	≥1200	≥800	7.8	8.4
HS1200	92/100	1200	35	1.35	Satin 12HS	≥96	18*13	≥1200	≥1000	7.8	8.4
STP42	92	1420	42	2	Plain	≥96	15*6	≥150	≥100	5.4	8.6
STP52	92	1750	52	3	Twill	≥96	12*8	≥500	≥200	5.4	8.6